Seawater is the harshest natural electrolyte: roughly 19,000 ppm chloride plus wet-dry cycling and crevices. Here the first criterion is not strength — it is whether the material survives crevice corrosion.

Describe Your Application View Products

Typical Parts and Material Selection

Part	Grade	Surface / Size	Watch Out For
Deck railing / fittings	316L	Tube / profile, polished	Salt spray, post-weld passivation
Seawater piping	2205 / 6Mo	Seamless / welded pipe	Pitting, flow erosion
LNG tank inner shell	304L / 304	Plate 8–50 mm	Low-temperature toughness, class approval
Interior / galley equipment	304 / 316L	0.8–2 mm, 2B/HL	Cleanability, fingerprint resistance
Fasteners / fixings	316 / 2205	Bar / forging	Stress corrosion cracking

These are the common configurations.The actual choice depends on medium, temperature and welding method— the same part can move from 304 to 316L or 2205. Describing the operating conditions is more useful than naming a grade.

Three Real Constraints in This Industry

Crevice corrosion is the dominant failure

Under gaskets and at bracket-to-hull contacts, 304 shows rust within months. Design out the crevice (continuous welds, drain holes) and upgrade to 316L or 2205.

Confirm class approval early

DNV / ABS / LR / CCS each have their own approved material lists. A better grade that is not approved still fails inspection — check at the bidding stage.

Weld distortion accumulates at assembly

Thin interior parts deform and the error accumulates at final assembly. Pre-fabricate in sections with distortion-control fixtures and leave trimming allowance.